Casting damage repair, metal crack repair, maintenance, mechanical stitch method repair.
We will repair the cracks that have occurred in the metal equipment without applying heat. By not applying heat, thermal distortion will not occur, and issues such as secondary cracking will also not arise.
The "MS Method (Mechanical Stitch)" is a groundbreaking repair technique (Mechanical Stitching Method) that addresses metal cracks using mechanical methods. Since no heat is applied at all, there is no "thermal distortion." Residual stress does not occur in other areas, preventing secondary damage such as new cracks. Metal cracks are one of the concerns in equipment maintenance operations. In typical welding repair methods, the base material around the crack changes due to heat, leading to residual stress and distortion, which always carries the risk of "crack recurrence" and "secondary damage." **Features of the MS Method** - No hardening or residual stress from heat - Elimination of secondary damage - Maintenance of stable quality → Integrated system repairs using jigs, etc. → Accumulation of know-how, experience, and track record - Completion of construction in a short period → No significant decrease in equipment operating rates - Advantages in safety and environmental aspects → No use of fire, so there is no impact on the operating rates of other equipment or the environment For more details, please contact us.
- Company：日之出水道機器 メカニカルスティッチ部
- Price：Other